Aegis 3D™ Aluminum Core Composite Panel
Aegis3D is an improved panels developed by Our Company for the architectural facade, it is a new generation of advanced materials formed by pure metal materials, no glue, no plastic components, 100% environmental protection and fire prevention, much sturdier, provides a range of re-cladding options for building facades and internal wall cladding systems.
DIMENSION
|
THICKNESS |
WIDTH(mm) |
LENGTH(mm) |
FINISHES |
|---|---|---|---|
| 2440 |
Mill finish |
||
| 4mm | 1000 | 2700 |
Solid / Metallic coating |
| 5mm | 1220 | 3200 |
Sparkling coating |
| 6mm | 1250 | 4000 |
Brushed & Wood-look |
| 7mm | 1500 |
customized |
KEY BENEFITS
DEEMED NON-COMBUSTIBLE
Aegis3D is one of few aluminium
panels globally that is deemed
non-combustible under the BCA whentested to AS1530.1 & AS1530.3, No combustibility, No toxic fumes.
CODEMARK
Aegis3D is ABCB CodeMark certified to comply with the Building Code of Australia ensuring that customers are
specifying a quality assured product.
BUILDING BEAUTIFICATION
Unparalleled flatness, Ultra strong, Ultralight (4.5kg/㎡). Available in a variety of finishes and textures, from 3mm to 10mm thickness.
PAINT SYSTEM
Aegis3D uses the highly recognized PVDF KYNAR 500 or PPG & FEVE paints known for their high durability, providing the optimum resistance to weather and industrial pollution.
REDUCE MATERIAL&LABOR COSTS
Coil continuous production technology, cost-effective and fast delivery, suitable for large projects. With pre-finished cassette panels, easy to assemble, reducing sheet metal, installation time and cost.
Warranty
Aegis3D™ has up to 15 year’s warranty when correctly installed and maintained.
FIRE RESISTANCE
|
TEST STANDARD |
ITEMS |
RESULT |
REGULARTORY INDICES |
|---|---|---|---|
|
NATA-AS1530.3 |
Ignitability Index |
PASS |
0 |
|
Spread of Flame |
PASS |
0 |
|
|
Heat Evolved |
PASS |
0 |
|
|
Smoke Developed |
PASS |
2 |
|
|
NATA-AS1530.1 |
DEEMED NON-COMBUSTIBLE MATERIALS |
||
TYPICAL COMPOSITION
|
TEST ITEM |
REF STANDARD |
TEST CONDITION |
TEST RESULT |
|---|---|---|---|
|
Pane weight |
|
|
4.5 kg /m2 |
|
Thickness |
|
|
4mm |
|
Width |
|
|
1250/1500 mm |
|
Thickness of aluminium face |
|
|
0.7mm |
|
Alloy |
|
|
3003 H24 |
|
Dry Film Thickness |
ASTM D1400 |
μm |
Avg,32; Min.30 |
|
Adhesion Original Sample After immersed in |
ASTM D3359-08 Method B |
Tape: 3M?610# Space 1mm |
5B |
|
5B,No visual change appeared on the coating |
|||
|
Gloss |
ASTM D2457-08 |
600 geometry |
31 |
|
Pencil Thickness |
ASTM D3363-05 |
Scratch hardness Pencil: Mitsubishi? |
2H |
|
Flexibility |
T-Bend, ASTM D4145 |
|
2 T-Bend; No pick-off |
|
Resistance to Acid and Alkali Reagent |
ASTM D1308-02(2007) |
Reagent:5% HCI Condition:23°C,24h |
Color difference ?E*ab=0.2,No blistering or chalking appeared on the sample’s surface |
|
Reagent:5% NaOH Condition:23°C,24h |
Color difference ?E*ab=0.3,No blistering or chalking appeared on the sample’s surface |
||
|
Core Shear properties |
ASTM C393/C393-11 |
|
Core shear ultimate strength:0.91 Mpa Facing stress:130.7 Mpa |
|
Tensile properties of facing aluminium panel |
ASTM E8/E8M-15a |
|
Tensile strength:172.9 Mpa Elongation: 8.4% |
|
Bending strength(Mpa) |
EN 485-2 ASTM D1781-98 (2012) |
|
186.5 N-mm/mm |
|
Peel strength after freeze-thaw cycle |
ASTM D1781-98 (2012) |
|
150 N-mm/mm |
|
Facing peel torque |
ASTM D1781-98 (2012) |
|
270 mm.N/mm |
|
Roll peel strength (N.mm/mm) |
EN 485-2 |
|
187.9N-mm/mm |
|
Flatwise compression strength (Mpa) |
EN 485-2 |
|
1.97 Mpa |
FIRE RESISTANCE
APPLICATION
Ceiling
Interior Decoration
Curtain Wall
COLOR
SL9010
Pure white
SL42G
High glossy white
SL9002
Stone White
SL7035
Foggy white
SL7001
Silver gray
SL7035
Light gray
SL7022
Deep gray
SL17
Black
SL40
Blue
SL50
Green
SL20
Yellow
SL30
Red
SL1401
Red Granite
White Granite
Coffee-colored reticulated granite
SL1403
White Granite
SL1404
White Marble
SL1301
Teak Texture
SL1302
Black larch Texture
SL1303
Annatto Texture
SL1304
White Larch Texture
SL1305
Bamboo Texture
SL1306
Maple Texture
SL1307
Sakuragi Texture
SL1308
Birch Texture
Subscribe to our newsletter to receive exclusive information about us and our services